Growth of High Permittivity Dielectrics by High Pressure Sputtering from Metallic Targets (Springer Theses)

This thesis describes the fabrication of metal-insulator-semiconductor (MIS) structures using very high permittivity dielectrics (based on rare earths) grown by high-pressure sputtering from metallic targets. It demonstrates the possibility of depositing high permittivity materials (GdScO3) by means of high pressure sputtering from metallic targets using in situ plasma oxidation on Si and indium phosphate (InP) substrates. The advantage of this system is the high working pressure, which causes the particles to undergo multiple collisions and become thermalized before reaching the substrate in a pure diffusion process, thus protecting the semiconductor surface from damage. This work presents a unique fabrication using metallic targets and involving a two-step deposition process: a thin metallic film is sputtered in an Ar atmosphere and this film is then plasma oxidized in situ. It also demonstrates the fabrication of GdScO3 on Si with a permittivity value above 30 from metallic Gd and Sc targets. Since co-sputtering was not possible, a nanolaminate of these materials was deposited and annealed. The electrical properties of these devices show that the material is highly interesting from a microelectronic integration standpoint. Front Matter ....Pages i-xxiii Introduction (María Ángela Pampillón Arce)....Pages 1-20 Fabrication Techniques (María Ángela Pampillón Arce)....Pages 21-39 Characterization Techniques (María Ángela Pampillón Arce)....Pages 41-62 Thermal Oxidation of Gd2O3 (María Ángela Pampillón Arce)....Pages 63-75 Plasma Oxidation of Gd2O3 and Sc2O3 (María Ángela Pampillón Arce)....Pages 77-108 Gadolinium Scandate (María Ángela Pampillón Arce)....Pages 109-124 Interface Scavenging (María Ángela Pampillón Arce)....Pages 125-140 Gd2O3 on InP Substrates (María Ángela Pampillón Arce)....Pages 141-153 Conclusions and Future Work (María Ángela Pampillón Arce)....Pages 155-157 Back Matter ....Pages 159-164